Semiconductor integrated circuit device and a method of manufacturing the same

ABSTRACT

Provided are a manufacturing method of a semiconductor integrated circuit device, which comprises forming an interconnect trench and a contact hole in an interlayer insulating film formed over a first-level interconnect on a semiconductor substrate, forming a barrier film inside of the trench and hole so that its film thickness increases from the center of the bottom of the hole toward the sidewalls all around the bottom of the contact hole, forming a copper film over the barrier film, and forming the second-level interconnect and a connector portion (plug) by polishing by CMP; and the semiconductor integrated circuit device manufactured by this method. According to the present invention, the geometrically shortest pathway of an electric current flowing from the second-level interconnect toward the first-level interconnect through a connector portion (plug) does not coincide with a thin barrier film portion which has the lowest electric resistance so that a current pathway can be dispersed and concentration of electrons does not occur readily.

TECHNICAL FIELD

[0001] The present invention relates to a semiconductor integrated circuit device, particularly, to a technique effective when adapted to a connector portion between interconnects.

BACKGROUND OF THE INVENTION

[0002] With a recent tendency to miniaturization of interconnects and multilevel metallization in a semiconductor integrated circuit device, a so-called damascene technique for the formation of interconnects or the like by making a trench in an insulating film and then embedding inside of the trench with a conductive film has been under investigation.

[0003] This damascene technique includes a single damascene method of embedding a trench for an interconnect and a trench for connecting between interconnects by two different steps and a dual damascene method of simultaneously embedding these two trenches.

[0004] As a conductive film to be embedded in these trenches, a copper film or the like having a small resistance is used.

[0005] Inside of the trench, a conductive film having a barrier property (which will hereinafter be called “barrier film”) is formed in order to prevent diffusion, into an insulating film, of a metal such as copper constituting the conductive film to be embedded or to improve adhesion between the conductive film to be embedded and the insulating film.

[0006] For instance, in NIKKEI MICRODEVICES, PP 65 to 66(July, 2000), it is pointed out as a problem that upon formation of an underlying film on the inside wall of a hole by sputtering, sputter particles sashay at the peripheral part of a wafer, thereby deteriorating their covering property of the hole.

SUMMARY OF THE INVENTION

[0007] The present inventors have carried out an investigation on the improvement of reliability of interconnects or the like formed by the damascene technique and have found that the reliability of the damascene wiring has a close relation to the way how the barrier film is adhered inside of the trench.

[0008] Described specifically, the barrier film is required to have a sufficient thickness in order to prevent diffusion, in an insulating film, of a metal such as copper constituting a conductive film to be embedded in a trench and to improve adhesion of the conductive film to be embedded in the trench with the insulating film.

[0009] When the barrier film has poor coverage property, thickness of the barrier film varies on the bottom or sidewalls of the trench. If the entirety of the barrier film is formed thick to prevent such unevenness, an aspect ratio of a hole to be embedded with a conductive film becomes large, causing embedding failure of the conductive film.

[0010] The barrier film has a higher resistance than the conductive film to be embedded in the trench. If the barrier film is made excessively thicker, the resistance of an interconnect or connector portion becomes large, thereby disturbing a high-speed operation of a semiconductor integrated circuit device.

[0011] The barrier film is thus required to have a thickness not greater than a predetermined thickness. If some portions of the barrier film are thin owing to uneven thickness, they provide a current pathway because of a smaller resistance at these portions. Particularly at contact holes, if the shortest distance of a current pathway and such a portion coincide each other, concentration of electrons occurs. As a result, so-called electromigration, that is, attraction of metal atoms from such portions by electrons occurs. Voids appear at portions after the metal atoms have transferred and connection failure or disconnection occurs.

[0012] An object of the present invention is to optimize the structure of a connector portion for connecting interconnects, hereby improving electromigration properties.

[0013] Another object of the present ivention is to optimize the structure of a barrier film at a connector portion between interconnects, thereby improving the characteristics of a semiconductor integrated circuit device.

[0014] The above-described objects and the other objects, and novel features of the present invention will be apparent from the description herein and accompanying drawings.

[0015] Outline of the typical inventions, among the inventions disclosed by the present application, will next be described briefly.

[0016] (1) In one aspect of the present invention, there is thus provided a semiconductor integrated circuit device which has a hole made in an insulating film formed over a semiconductor substrate; a first conductive film formed on the bottom and sidewalls of the hole and has a film thickness increasing from the center of the bottom toward the sidewalls of the hole; and a second conductive film formed over the first conductive film and embedded inside of the hole.

[0017] (2) In another aspect of the present invention, there is also provided a semiconductor integrated circuit device which has a hole made in an insulating film formed over a semiconductor substrate; a first conductive film formed on the bottom and sidewalls of the hole and is smaller in film thickness B at the center of the bottom of the hole than in film thickness A corresponding to a perpendicular line dropped toward the bottom of the hole from the shortest point from the corner of the bottom of the hole to the surface of the first conductive film; and a second conductive film formed over the first conductive film and embedded inside of the hole.

[0018] (3) In a further aspect of the present invention, there is also provided a semiconductor integrated circuit device which has a hole made in an insulating film formed over a semiconductor substrate; a first conductive film formed on the bottom and sidewalls of the hole and has a resistance lower at the center of the bottom of the hole than at a portion corresponding to a perpendicular line dropped toward the bottom of the hole from the shortest point from the corner of the bottom of the hole to the surface of the first conductive film; and a second conductive film formed over the first conductive film and embedded inside of the hole.

[0019] (4) In a still further aspect of the present invention, there is also provided a semiconductor integrated circuit device which has a first interconnect formed over a semiconductor substrate; a hole which is made in an insulating film formed over the first interconnect and having a bottom from which the first interconnect is exposed; a first conductive film formed on the bottom and sidewalls of the hole; a second conductive film formed over the first conductive film and embedded therewith inside of the hole; and a second interconnect formed over the second conductive film, wherein a site at which a shortest pathway from the first interconnect to the second interconnect through the first and second conductive films cuts across the first conductive film does not coincide with the lowest resistance site of the first conductive film.

[0020] (5) In a still further aspect of the present invention, there is also provided a semiconductor integrated circuit device, which comprises a first interconnect formed over a semiconductor substrate, an insulating film formed over the first interconnect, a hole which is made in the first interconnect and the insulating film and has a bottom positioned deeper than the surface of the first interconnect, a first conductive film which is formed on the bottom and sidewalls of the hole and is greater in the film thickness E of the sidewall portion of the hole contiguous to the surface of the first interconnect than in the film thickness B at the center of the bottom of the hole, and a second conductive film formed over the first conductive film and is embedded therewith inside of the hole.

BRIEF DESCRIPTION OF THE DRAWINGS

[0021]FIG. 1 is a fragmentary cross-sectional view of a substrate for illustrating a manufacturing method of a semiconductor integrated circuit device according to Embodiment 1 of the present invention;

[0022]FIG. 2 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 1 of the present invention;

[0023]FIG. 3 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 1 of the present invention;

[0024]FIG. 4 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 1 of the present invention;

[0025]FIG. 5 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 1 of the present invention;

[0026]FIG. 6 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 1 of the present invention;

[0027]FIG. 7 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 1 of the present invention;

[0028]FIG. 8 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 1 of the present invention;

[0029]FIG. 9 is a fragmentary cross-sectional view of a substrate of the semiconductor integrated circuit device for showing the effects of the Embodiment 1 of the present invention;

[0030]FIG. 10 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 1 of the present invention;

[0031]FIG. 11 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 1 of the present invention;

[0032]FIG. 12 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 1 of the present invention;

[0033]FIG. 13 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 1 of the present invention;

[0034]FIG. 14 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 1 of the present invention;

[0035]FIG. 15 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 1 of the present invention;

[0036]FIG. 16 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 1 of the present invention;

[0037]FIG. 17 is a fragmentary cross-sectional view of a substrate of the semiconductor integrated circuit device for illustrating the effect of Embodiment 1 of the present invention;

[0038]FIG. 18 is a fragmentary cross-sectional view of a substrate of the semiconductor integrated circuit device for illustrating the effect of Embodiment 1 of the present invention;

[0039]FIG. 19 is a fragmentary cross-sectional view of a substrate of the semiconductor integrated circuit device for illustrating the effect of Embodiment 1 of the present invention;

[0040]FIG. 20(a) is a fragmentary plain view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 1 of the present invention, and FIG. 20(b) is its fragmentary cross-sectional view;

[0041]FIG. 21(a) is a fragmentary plain view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 1 of the present invention, and FIG. 21(b) is its fragmentary cross-sectional view;

[0042]FIG. 22(a) is a fragmentary plain view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 1 of the present invention, and FIG. 22(b) is its fragmentary cross-sectional view;

[0043]FIG. 23(a) is a fragmentary plain view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 1 of the present invention, and FIG. 23(b) is its fragmentary cross-sectional view;

[0044]FIG. 24(a) is a fragmentary plain view of a substrate of the semiconductor integrated circuit device for illustrating the effect of Embodiment 1 of the present invention, and FIG. 24(b) is its fragmentary cross-sectional view;

[0045]FIG. 25(a) is a fragmentary plain view of a substrate for illustrating the semiconductor integrated circuit device according to Embodiment 1 of the present invention, and FIG. 25(b) is its fragmentary cross-sectional view;

[0046]FIG. 26 is a fragmentary plain view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 1 of the present invention;

[0047]FIG. 27 is a schematic view illustrating an apparatus used for manufacturing the semiconductor integrated circuit device according to Embodiment 1 of the present invention;

[0048]FIG. 28 is an explanatory view of an effect of Embodiment 1 of the present invention;

[0049]FIG. 29 is an explanatory view of another effect of Embodiment 1 of the present invention;

[0050]FIG. 30 is an explanatory view of a further effect of Embodiment 1 of the present invention;

[0051]FIG. 31 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 1 of the present invention;

[0052]FIG. 32 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 1 of the present invention;

[0053]FIG. 33 is a fragmentary cross-sectional view of a substrate for illustrating a manufacturing method of a semiconductor integrated circuit device according to Embodiment 2 of the present invention;

[0054]FIG. 34 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 2 of the present invention;

[0055]FIG. 35 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 2 of the present invention;

[0056]FIG. 36 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 2 of the present invention;

[0057]FIG. 37 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 2 of the present invention;

[0058]FIG. 38 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 2 of the present invention;

[0059]FIG. 39 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 2 of the present invention;

[0060]FIG. 40 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 2 of the present invention;

[0061]FIG. 41 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 2 of the present invention;

[0062]FIG. 42 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 2 of the present invention;

[0063]FIG. 43 is a fragmentary cross-sectional view of a substrate for illustrating a manufacturing method of a semiconductor integrated circuit device according to Embodiment 3 of the present invention;

[0064]FIG. 44 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 3 of the present invention;

[0065]FIG. 45 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 3 of the present invention;

[0066]FIG. 46 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 3 of the present invention;

[0067]FIG. 47 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 3 of the present invention;

[0068]FIG. 48 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 3 of the present invention;

[0069]FIG. 49 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 3 of the present invention;

[0070]FIG. 50 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 3 of the present invention;

[0071]FIG. 51 is a fragmentary cross-sectional view of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 3 of the present invention; and

[0072]FIG. 52 is a fragmentary cross-sectional view of a substrate of the semiconductor integrated circuit device for explaining the effect of Embodiment 3 of the present invention.

DETAILED DESCRIPTION OF THE INVENTION

[0073] Embodiments of the present invention will hereinafter be described specifically based on accompanying drawings. In all the drawings for describing the below-described embodiments, members having like function will be identified by like reference numerals and overlapping descriptions will be omitted

Embodiment 1

[0074] The semiconductor integrated circuit device according to one Embodiment of the present invention will be described in accordance with its manufacturing method. FIGS. 1 to 18, 20 to 26, 31 and 32 are fragmentary cross-sectional or fragmentary plain views of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 1 of the present invention.

[0075] First, as illustrated in FIG. 1, an n channel MISFET (Metal Insulator Semiconductor Field Effect Transistor) Qn and a p channel MISFETQp are formed as one example of a semiconductor element.

[0076] One example of the formation process of these MISFET will next be described.

[0077] A semiconductor substrate 1 made of, for example, p type single crystal silicon is etched to form a trench therein. An insulating film, for example, a silicon oxide film 7 is then embedded inside of the trench, whereby an isolation region 2 is formed. This isolation region 2 defines an active region in which MISFET is to be formed.

[0078] After ion implantation of a p type impurity and an n type impurity into the semiconductor substrate (which will hereinafter be called “substrate” simply) 1, these impurities are diffused by heat treatment to form a p type well 3 and an n type well 4. By thermal oxidation, a clean gate insulating film 8 is formed over the surface of each of the p type well 3 and n type well 4.

[0079] Over the gate insulating film 8, a low-resistance polycrystalline silicon film 9 a, a thin WN (tungsten nitride) film (not illustrated) and a W (tungsten) film 9 c are deposited successively as conductive films, followed by a silicon nitride film 10 thereover as an insulating film.

[0080] The silicon nitride film 10 is then etched by dry etching or the like to leave it in a region in which a gate electrode is to be formed. With the remaining silicon nitride film 10 as a mask, the W film 9 c, WN film (not illustrated) and polycrystalline film 9 a are etched by dry etching or the like, whereby a gate electrode 9 formed of the polycrystalline film 9 a, WN film (not illustrated) and W film 9 c is formed.

[0081] By ion implantation of an n type impurity into the p type well 3 extending both sides of the gate electrode 9 to form n⁻ type semiconductor regions 11, while by ion implantation of a p type impurity into the n type well 4 to form p⁻ type semiconductor regions 12.

[0082] A silicon nitride film is then deposited over the substrate 1 as an insulating film, followed by anisotropic etching, whereby sidewall spacers 13 are formed on the sidewalls of the gate electrode 9.

[0083] By ion implantation of an n type impurity to the p type well 3, n⁺ type semiconductor regions 14 (source and drain) having a higher impurity concentration than the n⁻ type semiconductor regions 11 are formed, while by ion implantation of a p type impurity to the n type well 4, p⁺ type semiconductor regions 15 (source and drain) having a high impurity concentration than the p⁻ type semiconductor regions 12 are formed.

[0084] By the steps so far described, the n channel type MISFETQn and p channel type MISFETQp having an LDD (Lightly Doped Drain) structure and equipped with source and drain are formed.

[0085] Next, an interconnect for electrically connecting the MISFETQn and Qp will be formed. Steps for forming them will next be described.

[0086] First, as illustrated in FIG. 1, a silicon oxide film is deposited, as an insulating film, over the MISFETQn and Qp by CVD (Chemical Vapor Deposition). The surface of the silicon oxide film is then polished by chemical mechanical polishing (CMP) to planarize the surface, whereby an interlayer insulating film TH1 is formed.

[0087] Over the interlayer insulating film TH1, a photoresist film (not illustrated. This film will hereinafter be called “resist film”, simply) is formed. With this resist film as a mask, the interlayer insulating film TH1 is etched to form a contact hole C1 over each of the n⁺ type semiconductor regions 14 and p⁺ type semiconductor regions 15 over the main surface of the semiconductor substrate 1.

[0088] A plug P1 is then formed in the contact hole C1 by depositing, over the interlayer insulating film TH1 including the inside of the contact hole C1, a tungsten (W) film as a conductive film by CVD and then polishing this tungsten film by CMP until the interlayer insulating film THE is exposed. Alternatively, this plug P1 may be formed to have a laminate structure of a barrier film—which has a single layer of a titanium nitride (TiN) film or a titanium (Ti) film, or a laminate film thereof—and a tungsten film.

[0089] As illustrated in FIG. 2, a silicon nitride film H1 a serving as an etching stopper and a silicon oxide film H1 b are deposited successively by CVD as an insulating film over the interlayer insulating film TH1 and plug P1, whereby an interconnect-trench-forming insulating film H1 made of these films is formed. The interconnect-trench-forming insulating film H1 in a region in which a first-level interconnect is to be formed is etched to form an interconnect trench HM1. Instead of the silicon oxide film H1 b, a silicon oxide film containing fluorine (F) may be used as an insulating film of a low dielectric constant. Another insulating film of a low dielectric constant or a coating type insulating film is also usable. The silicon nitride film H1 a is utilized as an etching stopper upon the above-described etching.

[0090] Over the interconnect-trench-forming insulating film H1 including the inside of the interconnect trench HM1, a barrier film M1 a made of titanium nitride is deposited by sputtering. Then, a copper film M1 b, as a conductive film, is formed over the barrier film M1 a by electroplating. Prior to the formation of the copper film M1 b by electroplating, a thin copper film may be formed by sputtering or CVD as a seed film for electroplating.

[0091] After heat treatment of the copper film M1 b, the copper film M1 b and barrier film M1 a outside of the interconnect trench HM1 are removed by CMP, whereby a first-level interconnect M1 having the copper film M1 and barrier film M1 a is formed.

[0092] As illustrated in FIG. 3, a silicon nitride film TH2 a, a silicon oxide film TH2 b, a silicon nitride film TH2 c and a silicon oxide film TH2 d are deposited successively, as insulating films, by CVD over the first-level interconnect M1, whereby an interlayer insulating film TH2 is formed. Among these films, the silicon nitride film TH2 a has a function of preventing diffusion of copper which constitutes the first-level interconnect M1. The silicon nitride film TH2 a can be replaced with another insulating film if the film has a Cu diffusion preventing function. The silicon nitride film TH2 a is used as an etching stopper upon formation of a contact hole C2 which will be described later. The silicon nitride film TH2 c is utilized as an etching stopper upon formation of an interconnect trench HM2 which will be described later.

[0093] Over the interlayer insulating film TH2, a resist film (not illustrated) opened at a region in which a second-level interconnect is to be formed is formed. With this resist film as a mask, the silicon oxide film TH2 d and silicon nitride film TH2 c are etched from the interlayer insulating film TH2 to form the interconnect trench HM2.

[0094] Over the interlayer insulating film TH2 including the inside of the interconnect trench HM2, a first resist film (not illustrated) is deposited. The interconnect trench HM2 is embedded with the first resist film by etch back. A second resist film (not illustrated) opened at a connecting region of the first-level interconnect with the second-level interconnect is then formed over the first resist film. With this second resist film as a mask, the first resist film, the silicon oxide film TH2 b and silicon nitride film TH2 a are etched, whereby the contact hole C2 is formed.

[0095] Here, the formation of the interconnect trench HM2 is followed by the formation of the contact hole C2. Alternatively, after formation of the contact hole C2 by etching the silicon nitride film TH2 a, silicon oxide film TH2 b, silicon nitride film TH2 c and silicon oxide film TH2 d from a connecting region of the first-level interconnect with the second-level interconnect, the interconnect trench HM2 may be formed by etching the silicon oxide film TH2 d and silicon nitride film TH2 c from a region in which the second interlevel interconnect is to be formed.

[0096] As illustrated in FIG. 4, over the interlayer insulating film TH2 including the insides of the contact hole 2C and interconnect trench HM2, the below-described refractory metal such as titanium (Ti) is deposited to form a barrier film PM2 a. As the refractory metal, at least one of or an alloy of titanium, tantalum (Ta), tantalum nitride (TaN), titanium nitride (TiN), tungsten (W), tungsten nitride, titanium silicide nitride and tungsten silicide nitride is usable. It is also possible to use a laminate film obtained by stacking the above-described films one after another.

[0097] At this time, the barrier film PM2 a is formed to have a structure as described below.

[0098]FIGS. 5 and 7 are enlarged views of the vicinity of the contact hole C2, which is a right one of three contact holes C2 in FIG. 4. FIG. 6 is a fragmentary plain view of the substrate illustrated in FIG. 5 or 7. FIG. 5 corresponds to the cross-section taken along a line A-A of FIG. 6, while FIG. 7 corresponds to the cross-section taken along a line B-B of FIG. 6. Although no particular limitation is imposed, the width of the interconnect trench HM2 is formed to be substantially equal to that of the interconnect trench HM1 in this Embodiment. In FIG. 6, however, the width of the interconnect trench HM1 is illustrated smaller than that of the interconnect trench HM2 in order to facilitate observation of the drawing.

[0099] As illustrated in FIGS. 5 and 7, the barrier film PM2 a is formed along the bottom and sidewalls of the interconnect trench HM2 and contact hole C2.

[0100] In the contact hole C2, the barrier film PM2 a on the bottom thereof is formed to increase its thickness from the center of the bottom toward the sidewalls. This increase in thickness of the barrier film PM2 a on the bottom of the contact hole C2 from the center of the bottom toward the sidewalls is applied to all around the bottom. As illustrated in FIG. 8, which is a partially enlarged view of the bottom of the contact hole C2 in FIG. 7, supposing that the thickness of the barrier film at the center of the bottom of the contact hole C2 is B, film thickness A which is a film thickness of the end portion, in the direction of the sidewalls, of the bottom of the contact hole C2 is made greater than the film thickness B (A≧B). Moreover, the film thickness C, which is a film thickness on the sidewalls at a bottom portion of the contact hole C2 is made greater than the film thickness B (C≧B).

[0101] The film thickness B or film thickness D, which is a film thickness of the barrier film at the upper portion of each of the sidewalls of the contact hole C2, is formed to be at least the minimum thickness permitting maintenance of barrier properties. Below the barrier film PM2 a on the bottom of the contact hole C2, the first-level interconnect M1 is formed so that the barrier film PM2 a at such a position is not always required to have a film thickness large enough to maintain barrier properties. As illustrated in FIG. 9, however, there sometimes occurs misalignment between the first-level interconnect M1 and the contact hole C2 due to mask misalignment. The film thickness B is therefore desirably adjusted to at least the minimum film thickness permitting maintenance of barrier properties. In FIG. 9, PM2 b and PM2 c are copper films (their boundary is not illustrated in the drawing) over the barrier film PM2 a. TH3 a and TH3 b are insulating films over the copper films (PM2 b,PM2 c).

[0102] As illustrated in FIG. 10, after formation of a copper film PM2 b, as a seed film for electroplating, over the barrier film PM2 a by sputtering or CVD, a copper film PM2 c is formed, as a conductive film, over the copper film PM2 b by electroplating.

[0103] After heat treatment of the copper films PM2 b and PM2 c, the copper films PM2 b, PM2 c and barrier film PM2 a outside the interconnect trench HM2 and contact hole C2 are removed by CMP to form a second-level interconnect M2 and a connector portion (plug) P2 between the first-level interconnect and the second-level interconnect as illustrated in FIG. 11. FIGS. 12 and 13 are enlarged views of the vicinity of the contact hole C2 in FIG. 11. FIGS. 12 and 13 correspond to the A-A cross-sectional view and B-B cross-sectional view of FIG. 6, respectively.

[0104] The essential points in the structure of the second-level interconnect M2, connector portion (plug) P2 and first-level interconnect M1 will next be described briefly.

[0105] The second-level interconnect M2 and connector portion (plug) P2 are each made of the copper films PM2 b, PM2 c and barrier film PM2 a. As illustrated in FIG. 12, the second-level interconnect M2 extends to the left side, starting from the connector portion (plug) 2, while the first-level interconnect M1 extends to the right side, starting from the connector portion (plug) P2.

[0106] As described above, the barrier film PM2 a on the bottom of the contact hole C2 increases its thickness from the center of the bottom toward the sidewalls. In other words, the barrier film PM2 a has a decline towards the center of the bottom from the sidewalls of the contact hole C2. As illustrated in FIG. 14, which is a partially enlarged view of the bottom of the contact hole C2 in FIG. 13, the film thickness B of the barrier film PM2 a on the center of the bottom of the contact hole C2 is smaller than the film thickness A which is the film thickness, at the end portion in the direction of the sidewalls, on the bottom of the contact hole C2 (A≧B). The film thickness A can be determined, for example, by dropping a perpendicular line toward the bottom of the contact hole C2 from the end of the shortest distance L between from the corner of the bottom of the contact hole C2 to the surface of the barrier film PM2 a.

[0107] The actual surface of the barrier film is, as illustrated in FIG. 15, is curved at the corner of the bottom of the contact hole C2. When the contact hole C2 has a curved corner, the above-described shortest distance L can be determined by using, as a starting point, the intersection between the extension of the side line of the contact hole C2 and the extension of the bottom line.

[0108] In the case where electric current (i) flows from the second-level interconnect M2 to the first-level interconnect M1 via such a connector portion (plug) P2, an electron (e) flows, as illustrated in FIG. 17, through a route Ru1 which extends from the lower right to the upper left of the connector portion (plug) P2, because this route becomes the geometrically shortest route. An electron (e) flows, as illustrated in FIG. 18, toward the first-level interconnect M1 via the center of the connector portion (plug) P2, because the electric resistance of a thin portion of the barrier film PM2 a becomes lowest.

[0109] According to this Embodiment, the geometrically shortest route (route Ru1) of electric current from the second-level interconnect M2 to the first-level interconnect M1 does not coincide with a thin portion of the barrier film PM2 a at which the electric resistance becomes lowest so that a current route can be dispersed. Accordingly, concentration of electrons (e) do not occur easily, making it possible to improve electromigration properties.

[0110] As illustrated in FIG. 19, upon formation of the barrier film PM2 a′, variations in film thickness appear inside of the contact hole C2. Variations are particularly large when the film is formed by sputtering, because how sputter particles (Ti particles, in this case) scattered from a target enter the contact holes C2 differs, depending on the position of the contact hole on the wafer.

[0111] When the contact hole exists on the left edge of the wafer, the barrier film PM2 a′ is formed thick on the left sidewall of the contact hole C2 and is formed thin on its right sidewall as illustrated in FIG. 19. On the bottom of the contact hole C2, the film thickness shows a gradual decrease from the left side toward the right side. Since in the contact hole on the left end of the wafer, sputter particles coming from the right direction enter more easily than those coming from the left direction, the barrier film PM2 a′ is formed thick on the left sidewall or left side of the bottom opposite to the coming direction of the sputter particles. When the contact hole exists on the right end of the wafer, on the other hand, the barrier film is formed thick on the right sidewall or right side of the bottom of the contact hole (refer to FIG. 1(a) of the above-described NIKKEI MICRODEVICES, p. 65(July 2000)).

[0112] When an electric current flows from the second-level interconnect M2 to the first-level interconnect M1 through the connector portion (plug) P2 as illustrated in FIG. 19, a pathway via the route Ru1 extending from the upper left toward the lower right of the connector portion (plug) P2 becomes a geometrically shortest route. At the same time, a thin portion of the barrier film exists in the lower right of the connector portion (plug) P2. Concentration of electrons (e) therefore occurs at such a portion. Electrons which pass through the above-described portion attract copper atoms constituting a copper film and with this portion as a starting point, peeling occurs at the interface between the copper films (PM2 b, PM2 c) and the barrier film PM2 a′. If the electric current is continuously passed, copper transfer becomes large, thereby forming a void, which becomes a cause of disconnection. Such a phenomenon of transfer of metal atoms by momentum exchange between electrons flowing through a conductor and metal ions is called electromigration.

[0113] As described above, when the barrier film PM2 a′ has a shape as illustrated in FIG. 19, the geometrically shortest route Ru1 of electric current crosses over a thin portion (a portion whose electric resistance becomes lowest) of the barrier film, causing a deterioration in electromigration properties.

[0114] In this Embodiment, on the other hand, the barrier film PM2 a on the bottom of the contact hole C2 is formed to have a thickness increasing from the center of the bottom toward the sidewalls. The geometrically shortest route Ru1 of electric current therefore does not cross over a thin portion (a portion whose electric resistance becomes lowest) of the barrier film, thereby preventing concentration of electrons to this portion. As a result, improvement in electromigration properties can be attained.

[0115] In this Embodiment, as illustrated in FIGS. 12 and 13, the barrier film PM2 a on the bottom of the contact hole C2 is formed to have a thickness increasing from the center of the bottom toward the sidewalls all round the bottom of the contact hole C2 so that the above-described effect is available even if the first-level interconnect M1 extends to any direction relative to the second-level interconnect M2.

[0116] Described specifically, as illustrated in FIGS. 20 to 23, the first-level interconnect Ml and the second-level interconnect M2 form various angles. For example, FIGS. 20, 21, 22 and 23 illustrate the cases where angles formed between them are 180°, 0(360)°, 90°, and 270°, respectively. In each of FIGS. 20 to 23, the upper drawing (a) is a plain view illustrating the relationship between the pattern of the first-level interconnect M1 and the pattern of the second-level interconnect M2, while the lower drawing (b) is a cross-sectional view taken along a line C-C of the plain view (a).

[0117] An increase in the thickness of the barrier film PM2 a from the center of the bottom toward the sidewalls all around the bottom of the contact hole C2 as in this Embodiment makes it possible to improve electromigration properties as illustrated in FIGS. 20 to 23 irrespective of the angle formed between the pattern of the first-level interconnect M1 and the pattern of the second-level interconnect M2. Of course, the angle formed between the pattern of the first-level interconnect M1 and the pattern of the second-level interconnect M2 is not limited to the one shown in FIGS. 20 to 23. Even when the pattern of the first-level interconnect M1 and the pattern of the second-level interconnect M2 cross diagonally, improvement can be brought about. When the barrier film PM2 a is formed thick only on the left side of the contact hole C2 as illustrated in FIG. 19, on the other hand, a deterioration in electromigration properties occurs, in among extending directions of the first-level interconnects (a1) to (d1), in directions (a1,c1,d1) other than the left direction (b1). In FIG. 24 for facilitating understanding of the effect of this Embodiment, the upper drawing (a) is a plain view illustrating the pattern of the first-level interconnect M1 and the lower drawing (b) is a cross-sectional view taken along a line C-C of the plain view.

[0118] According to this Embodiment, as illustrated in FIG. 25, even in the case where two interlevel interconnects M1 extend in the directions of (a1) and (b1) or (c1), and (a2) and (b2) or (c2), respectively relative to the second-level interconnect M2, the above-described effect is available because the film thickness is increased from the center of the bottom toward the sidewalls all around the bottom of the contact hole C2. FIG. 25 is a drawing for facilitating understanding of the effect of this Embodiment. In FIG. 25, the upper drawing (a) is a plain view illustrating the relationship between the pattern of the first-level interconnect M1 and the pattern of the second-level interconnect M2, while the lower drawing (b) is a cross-sectional view taken along a line C-C of the plain view.

[0119] Even when the second-level interconnects M2 is disposed as illustrated in FIG. 26 relative to a plurality of the first-level interconnects M1 connected with the n⁺ type semiconductor regions 14 (source, drain) and p⁺ type semiconductor regions 15 (source, drain) via plugs P1 as illustrated in FIG. 11, electromigration properties can be improved. For example, FIG. 11 corresponds to a cross-section taken along a line D-D of FIG. 26.

[0120] As described above, the film thickness C of the barrier film PM2 a on the bottom of the sidewalls of the contact hole C2 is greater than the film thickness B at the center of the bottom (Refer to FIGS. 8 and 14).

[0121] This film thickness C is determined, for example, by dropping a perpendicular line from the end portion of the shortest distance L, which extends from the bottom corner of the contact hole C2 toward the surface of the barrier film PM2 a, to the sidewalls of the contact hole C2.

[0122] The actual surface of the barrier film is, as illustrated in FIG. 15, is curved at the corner of the bottom of the contact hole C2. As illustrated in FIG. 16, when the corner of the contact hole C2 is curved, the above-described shortest distance L can be determined by using, as a starting point, an intersection of the extended side line of the contact hole C2 with the extended bottom line.

[0123] By setting the film thickness C greater than the film thickness B, concentration of electrons can be prevented even if overetching not greater than the film thickness A is conducted upon formation of the contact hole C2. This effect will be described in detail in Embodiment 3 so that further description is omitted here.

[0124] In the next place, one example of the formation step of the barrier film PM2 a and controlling method of the film thicknesses A and B will be described.

[0125]FIG. 27 is a schematic view of an ion bias sputtering apparatus 101 used for the formation of the barrier film PM2 a. As illustrated in FIG. 27, the substrate 1 (wafer) having the contact hole C2 formed therein, which substrate is illustrated in FIG. 3, is held by a supporter St and alternating voltage Ev has been applied (biased). Above the wafer, target Ta (in this case, a plate made of Ti) exists. Upon formation of the barrier film, the apparatus is under pressure-reduced condition and upon film formation, a gas for discharge such as argon (Ar) is injected into the apparatus. When a voltage is applied in this argon atmosphere, glow discharge occurs and the target Ta of the cathode is bombarded with ions in the plasma to displace sputter particles (in this case, Ti particles). These displaced particles are deposited in the contact hole on the surface of the wafer, whereby a barrier film is formed.

[0126]FIG. 28 is a ratio (A/B) of the film thickness A to the film thickness B when the substrate bias [a.u.] to be applied to the substrate 1 is changed. As illustrated in the graph (a) of FIG. 28, the greater the substrate bias, the greater the film thickness ratio (A/B). When the substrate bias is 2 or greater, the film thickness ratio (A/B) becomes 1 or greater, in other words, A≧B. The point B represents a film thickness ratio (A/B) when the film is formed by ordinarily employed magnetron sputtering.

[0127] Upon film formation, it is preferred that the deposition rate is 50 nm/min, film forming pressure is 0.1 Pa or less, and film forming temperature falls within a range of from room temperature to 400° C. FIG. 28 is a graph of a film thickness ratio when the width of the interconnect trench HM2 is 0.18 μm and the aspect ratio of the contact hole C2 (sum of the interconnect depth and the depth of the connector portion/diameter of the connector portion) is 2.8.

[0128] Thus, by controlling the substrate bias, the film thickness ratio (A/B) can be controlled and conditions permitting adjustment of the film thickness ratio (A/B) to 1 or greater as described in this Embodiment can be selected. The conditions permitting adjustment of the film thickness ratio (A/B) to 1 or greater vary, depending on the size of the interconnect or connecting hole.

[0129]FIG. 29 shows a ratio (C/B) of the film thickness C to the film thickness B when the substrate bias [a.u.] to be applied to the substrate 1 is changed. As illustrated in FIG. 29(c), the greater the bias, the greater the film thickness ratio (C/B). When the bias is about 3 or greater, the film thickness ratio (C/B) becomes 1 or greater, that is, C≧B. The point d means a film thickness ratio (C/B) when the film is formed using ordinarily employed magnetron sputtering.

[0130] In order to satisfy both A≧B and C≧B, film formation must be carried out at a substrate bias of 3 or greater.

[0131]FIG. 30 is a graph showing the relationship between a cumulative failure [%] and stress time [a.u.] of a semiconductor integrated circuit device when a barrier film is formed using ordinarily employed magnetron sputtering under the conditions of A≦B and C≦B and when the film is formed under the conditions of A≧B and C≧B as described in this Embodiment. The graph (f) shows the former case where A≦B and C≦B, while the graph (g) shows the latter case where A≧B and C≧B. The term “stress time” as used herein means the time during which the semiconductor integrated circuit device is exposed to extreme conditions such as high temperature. As illustrated in the graph, a single digit improvement in the electromigration life can be attained by the constitution according to this Embodiment.

[0132] In the next place, steps for forming upper-level interconnects (third to fifth-level interconnects) over the second-level interconnect M2 will be described.

[0133] As illustrated in FIG. 31, an interlayer insulating film TH3 (silicon nitride film TH3 a, silicon oxide film TH3 b, silicon nitride film TH3 c and silicon oxide film TH3 d) is formed over the second-level interconnect M2 in a similar manner to that employed for the formation of the interlayer insulating film TH2, and an interconnect trench HM3 and contact hole C3 are formed in a similar manner to that employed for the formation of the interconnect trench HM2 and contact hole C2. Then, as in the barrier film PM2 a, and copper films PM2 g and PM2 c, a barrier film PM3 a and copper films PM3 b and PM3 c are formed, followed by polishing by CMP after heat treatment, whereby a third-level interconnect M and a connector portion (plug) P3 between the second-level interconnect and the third-level interconnect are formed. In short, the barrier film PM3 a in the contact hole C3 is formed to have a structure similar to that of the barrier film PM2 a. This means that the barrier film PM3 a on the bottom of the contact hole C3 is formed to have a film thickness increasing from the center of the bottom toward the sidewalls all around the bottom of the contact hole C3.

[0134] By forming interlayer insulating films TH4 and TH5, fourth-level and fifth-level interconnects M4 and M5, and connecting portions (plugs) P4 and P5 to have similar structures to the interlayer insulating film TH3, third-level interconnect M3 and connector portion (plug) P2, respectively, a five-layer interconnect is formed as illustrated in FIG. 32. Described specifically, in a contact hole C4 through which the fourth-level interconnect M4 and the third-level interconnect M3 are connected, a barrier film PM4 a on the bottom of the contact hole C4 is formed to have a film thickness increasing from the center of the bottom toward the sidewalls all around the bottom of the contact hole C4. In a contact hole C5 through which the fifth-level interconnect M5 and the fourth-level interconnect M4 are connected, the barrier film PM5 a on the bottom of the contact hole C5 is formed to have a film thickness increasing from the center of the bottom toward the sidewalls all around the bottom of the contact hole C5. PM4 b and PM5 b are copper films similar to PM3 b and PM2 b, while PM4 c and PM5 c are copper films similar to PM3 c and PM2 c.

[0135] After deposition of a silicon nitride film, as a copper diffusion preventive film, over the fifth-level interconnect MS, a laminate film PV of a silicon oxide film and a silicon nitride film is deposited as a protective film.

[0136] Although no particular limitation is imposed, the second-level interconnect M2 and fourth-level interconnect M4 are formed to extend mainly in the X direction, while the third-level interconnect M3 and fifth-level interconnect M5 are formed to extend mainly to a direction vertical to the X direction. With the first-level interconnect M1 to the fifth-level interconnect M5, MISFETQn and Qp are linked to constitute, for example, a logic circuit of microprocessor.

[0137] In this Embodiment, the first-level interconnect is formed from a copper film M1 b. As the first-level interconnect, a copper alloy (an alloy containing, in addition to copper, magnesium (Mg), silver (Ag), platinum (Pt), titanium (Ti), tantalum (Ta) or aluminum (Al)), silver or a silver alloy, gold (Au) or a gold alloy, or aluminum or an aluminum alloy (an alloy containing, in addition to aluminum, silicon (Si), copper, niobium (Nb) or titanium) may be used as a main material. In this Embodiment, the first-level interconnect is formed by the damascene method. Alternatively, after deposition of the above-described material over the interlayer insulating film TH1, it may be patterned into a desired shape by dry etching.

Embodiment 2

[0138] In Embodiment 1, the second-level interconnect M2 and connector portion (plug) 2 are formed by the dual damascene method. Alternatively, the single damascene method may be employed, as described below, to form them. A semiconductor integrated circuit device according to this Embodiment of the present invention will next be described in accordance with its manufacturing method. FIGS. 33 to 42 are fragmentary cross-sectional or fragmentary plain views of a substrate for illustrating the manufacturing method of the semiconductor integrated circuit device according to Embodiment 2 of the present invention. Steps until the formation of the first-level interconnect M1 are similar to those of Embodiment 1, which was described with reference to FIGS. 1 and 2, so that its description is omitted.

[0139] As illustrated in FIG. 33, a silicon nitride film TH2 a and a silicon oxide film TH2 b are deposited successively as insulating films by CVD over the first-level interconnect M1 and an interconnect-trench-forming insulating film H1, whereby an interlayer insulating film TH22 is formed. Of these films, the silicon nitride film TH2 a functions to prevent diffusion of copper constituting the first-level interconnect M1. It is also utilized as an etching stopper upon formation of a contact hole C2 which will be described later.

[0140] Over the interlayer insulating film TH22, a resist film (not illustrated) having an opening in a region in which a connector portion (plug) is to be formed is formed. With this resist film as a mask, the interlayer insulating film TH22 (silicon nitride film TH2 a and silicon oxide film TH2 b) are etched to form a contact hole C2.

[0141] Then, in a similar manner to that employed for the formation of the barrier film PM2 a in Embodiment 1, a barrier film P2 a is formed.

[0142] Described specifically, as illustrated in FIGS. 34 and 35, a refractory metal such as titanium (Ti) is deposited over the interlayer insulating film TH22 including the inside of this contact hole C2 to form the barrier film P2 a. Upon formation, the barrier film P2 a on the bottom is formed to have a film thickness increasing from the center of the bottom toward the sidewalls all around the bottom of the contact hole C2 (refer to FIGS. 5 to 7 in Embodiment 1). Supposing that the thickness of the barrier film at the center of the bottom of the contact hole C2 is B, film thickness A which is a thickness of the barrier film at end portions, in the direction of the sidewalls, of the bottom of the contact hole C2 is made greater than the film thickness B (A≧B). Moreover, the film thickness C on the bottom of each of the sidewalls of the contact hole C2 is made greater than the film thickness B (C≧B). FIG. 34 is an enlarged view of the vicinity of the contact hole C2, which is a right one among the contact holes C2 in FIG. 33, while FIG. 35 is a partially enlarged view of the bottom of the contact hole C2 in FIG. 34.

[0143] As illustrated in FIG. 36, after formation of a copper film P2 b on the barrier film P2 a by sputtering or CVD as a seed film for electroplating, a copper film P2 c is formed as a conductive film over the copper film P2 b by electroplating.

[0144] The copper films P2 b and P2 c are heat treated, followed by removal of the copper films P2 b and P2 c and barrier film P2 a outside the contact hole C2 by CMP to form a connector portion (plug) P2 between the first-level interconnect M1 and the second-level interconnect M2 as illustrated in FIG. 37. FIG. 38 and FIG. 40 are enlarged views of the vicinity of a contact hole C2 which is a right-side one among the three contact holes C2 in FIG. 37. FIG. 39 is a fragmentary plain view of the substrate shown in FIG. 38 and FIG. 40. FIG. 38 corresponds to a A-A cross-section of FIG. 39, while FIG. 40 corresponds to a B-B cross-section of FIG. 39. As illustrated in them, the connector portion (plug) P2 has a similar constitution to that of the connector portion (plug) P2 described in Embodiment 1.

[0145] As illustrated in FIG. 41, over the interlayer insulating film TH22 and plug P2, a silicon nitride film TH2 and a silicon oxide film TH2 d, as insulating films, are deposited successively by CVD to form an interconnect-trench-forming insulating film H22. Of these films, the silicon nitride film TH2 c serves as an etching stopper upon formation of an interconnect trench HM2 which will be described later.

[0146] Over the interconnect-trench-forming insulating film H22, a resist film (not illustrated) having an opening in a region in which a second-level interconnect is to be formed is formed. With this resist film as a mask, the interconnect-trench-forming insulating film H2 (silicon oxide film TH2 d and silicon nitride film TH2 c) is etched to form the interconnect trench HM2.

[0147] Over the interlayer insulating film TH2 including the inside of the interconnect trench HM2, a refractory metal, for example, Ti (titanium) is deposited to form a barrier film M2 a.

[0148] After formation of a copper film M2 b over the barrier film M2 a by sputtering or CVD as a seed film for electroplating, a copper film M2 c is formed thereover as a conductive film by electroplating.

[0149] The copper films M2 b and M2 c are heat treated, followed by removal of the copper films 2 b and M2 c and the barrier film M2 a outside the interconnect trench HM2 by CMP to form the second-level interconnect M2.

[0150] By repeating the formation of interlayer insulating films (TH23 to TH25), connector portions (P3 to P5), interconnect-trench-forming insulating films (H23 to H25) and interconnects (M3 to M5), a five-layer interconnect as illustrated in FIG. 42 is formed. They are formed in similar manners to those employed for the formation of the interlayer insulating film TH2, connecting portion (plug) P2, interconnect-trench-forming insulating film H22, and second-level interconnect M2.

[0151] After formation of a silicon nitride film, as a copper diffusion preventive film, over the fifth-level interconnect M5 as in Embodiment 1, a laminate film PV of a silicon oxide film and a silicon nitride film is formed by deposition as a protective film. By this, the barrier films P3 a, P4 a and P5 a on the bottoms of the contact holes C3, C4 and C5 are each formed to have a film thickness increasing from the center of the bottom toward the sidewalls all around the bottom of the contact hole as in Embodiment 1.

[0152] According to this Embodiment, the barrier film P2 a on the bottom of the contact hole C2 is formed to increase its thickness from the bottom of the contact hole toward its sidewalls as described in Embodiment 1. The geometrically shortest route of an electric current from the second-level interconnect M2 to the first-level interconnect M1 therefore does not cross over a thin portion (a portion whose electric resistance becomes the lowest) of the barrier film, whereby concentration of electrons to this portion can be prevented. As a result, electromigration properties can be improved.

[0153] By setting the film thickness C greater than the film thickness B, concentration of electrons can be prevented even if overetching not greater than the film thickness A is conducted upon formation of the contact hole C2.

Embodiment 3

[0154] The semiconductor integrated circuit device according to this Embodiment of the present invention will next be described in accordance with its manufacturing process. FIGS. 43 to 51 are fragmentary cross-sectional or fragmentary plain views of a substrate for illustrating the manufacturing process of the semiconductor integrated circuit device according to Embodiment 3 of the present invention. Since steps up to the formation of the first-level interconnect M1 are similar to those employed for Embodiment 1 which were described with reference to FIGS. 1 and 2, description of them are omitted.

[0155] As illustrated in FIG. 43, a silicon nitride film TH2 a, a silicon oxide film TH2 b, a silicon nitride film TH2 c and a silicon oxide film TH2 d are deposited successively by CVD as an insulating film over the first-level interconnect M1 and interconnect-trench-forming insulating film H1, whereby an interlayer insulating film TH2 is formed. Of these films, the silicon nitride film TH2 a has a function of preventing diffusion of copper constituting the first-level interconnect M1. It is also utilized as an etching stopper upon formation of a contact hole C2 which will be described later. The silicon nitride film TH2 c serves as an etching stopper upon formation of an interconnect trench HM2 which will be described later.

[0156] Over the interlayer insulating film TH2, a resist film (not illustrated) opened at a region in which a second interconnect is to be formed is formed. With this resist film as a mask, the silicon oxide film TH2 d and silicon nitride film TH2 c are etched from the interlayer insulating film TH2 to form the interconnect trench HM2.

[0157] Over the interlayer insulating film TH2 including the inside of the interconnect trench HM2, a first resist film (not illustrated) is deposited. The interconnect trench HM2 is embedded with the first resist film by etch back. A second resist film (not illustrated) opened at a connecting region of the first-level interconnect with the second-level interconnect is then formed over the first resist film. With this second resist film as a mask, the first resist film, silicon oxide film TH2 b and silicon nitride film TH2 a are etched, whereby the contact hole (C2) is formed. As described in Embodiment 1, the interconnect trench HM2 may be formed after the formation of the contact hole C2.

[0158] If overetching is conducted upon formation of this contact hole C2, the bottom of the contact hole C2 comes at a position deeper than the surface of the first-level interconnect M1 as illustrated in FIG. 43.

[0159] As illustrated in FIG. 44, a refractory metal such as Ti (titanium) is deposited over the interlayer insulating film TH2 including the insides of the contact hole C2 and interconnect trench HM2, whereby a barrier film PM2 a is formed.

[0160] The barrier film PM2 a is formed to have the below-described structure.

[0161]FIGS. 45 and 47 are each an enlarged view of the vicinity of the contact hole C2 in FIG. 44. FIG. 46 is a fragmentary plain view of the substrate illustrated in FIGS. 45 and 47. FIG. 45 illustrates a A-A cross-section of FIG. 46, while FIG. 47 corresponds to a B-B cross-section of FIG. 46. As illustrated in FIGS. 45 and 47, the barrier film PM2 a is formed along the bottom and sidewalls of the interconnect trench HM2 or contact hole C2.

[0162] In the contact hole C2, the barrier film PM2 a on the bottom thereof is formed to increase its film thickness from the center of the bottom of the contact hole C2 toward the sidewalls all around the bottom of the contact hole C2. As illustrated in FIG. 48, which is a partially enlarged view of the bottom of the contact hole C2 in FIG. 47, supposing that the thickness of the barrier film at the center of the bottom of the contact hole C2 is B, film thickness A which is a thickness on the end portion, in the direction of the sidewall, of the bottom of the contact hole C2 is made greater than the film thickness B (A≧B). The barrier film on the sidewalls increases its thickness from a portion above a position contiguous to the surface F of the first-level interconnect M1 toward the bottom of the contact hole C2. The film thickness E of the barrier film PM2 a contiguous to the surface F of the first-level interconnect Ml is the thickness on the sidewall and is greater than the film thickness B (E≧B).

[0163] As illustrated in Embodiment 1, the film thickness B or the film thickness D of the barrier film on the sidewalls of the contact hole C2 must be adjusted to at least the minimum thickness permitting maintenance of barrier properties.

[0164] As illustrated in FIG. 49, after formation of a copper film PM2 b over the barrier film PM2 a by sputtering or CVD as a seed film for electroplating, a copper film PM2 c is formed, as a conductive film, over the copper film PM2 b by electroplating.

[0165] After heat treatment of the copper films PM2 b and PM2 c, the copper films PM2 b, PM2 c and barrier film PM2 a outside the interconnect HM2 and contact hole C2 are removed by CMP to form a second-level interconnect M2 and a connector portion (plug) P2 between the first-level interconnect and the second-level interconnect. FIGS. 50 and 51 are enlarged views of the vicinity of the contact hole C2 in FIG. 49. FIGS. 50 and 51 correspond to the A-A cross-section and B-B cross-section of FIG. 46, respectively.

[0166] The essential points in the structure of the second-level interconnect M2, connector portion (plug) and first-level interconnect M1 will next be described.

[0167] The second-level interconnect M2 and connector portion (plug) P2 are each made of the copper films PM2 b, PM2 c and barrier film PM2 a. As illustrated in FIG. 50, the second-level interconnect M2 extends to the left side, starting from the connector portion (plug) 2, while the first-level interconnect M1 extends to the right side, starting from the connector portion (plug) P2.

[0168] As described above, the barrier film PM2 a on the bottom of the contact hole C2 increases its thickness from the center of the bottom toward the sidewalls. In other words, the barrier film PM2 a has a decline toward the center of the bottom from the sidewalls of the contact hole C2. The film thickness B of the barrier film on the center of the bottom of the contact hole C2 is smaller than the film thickness A which is a film thickness at an end portion, in the direction of sidewalls, of the bottom of the contact hole C2 (A≧B). The film thickness A can be determined, for example, by dropping a perpendicular line toward the bottom of the contact hole C2 from the end of the shortest distance L between from the corner of the bottom of the contact hole C2 to the surface of the barrier film.

[0169] The actual surface of the barrier film is, as illustrated in FIG. 15, curved at the corner of the bottom of the contact hole. When the contact hole has a curved corner as illustrated in FIG. 16, the above-described shortest distance L can be determined by using, as a starting point, the intersection between the extended side line and extended bottom line of the contact hole C2.

[0170] The connector portion (plug) P2 has a bottom at a position deeper by an overetching amount OE from the surface F of the first-level interconnect M1 and the film thickness E of the barrier film PM2 a at a portion contiguous to the surface F of this first-level interconnect M1 is greater than the film thickness B (refer to FIG. 48).

[0171] According to this Embodiment, the film thickness E is greater than the film thickness B so that the geometrically shortest route Ru1 (refer to FIG. 52) when an electric current flows from the second-level interconnect M2 toward the first-level interconnect M1 does not cross over a thin portion of the barrier film at which the electric resistance becomes the lowest.

[0172] According to this Embodiment, the geometrically shortest route of electric current from the second-level interconnect M2 to the first-level interconnect M1 does not coincide with a thin portion of the barrier film PM2 a at which the electric resistance becomes lowest so that a current route can be dispersed. Accordingly, concentration of electrons (e) do not occur easily even if overetching occurs upon formation of the contact hole C2, making it possible to improve electromigration properties.

[0173] As described in Embodiment 1, when the barrier film has some variations in its thickness inside of the contact hole (refer to FIG. 19), and moreover, overetching occurs upon formation of the contact hole C2, the geometrically shortest route (route Ru1) of an electric current crosses over the sidewalls of the barrier film PM2 a′ as illustrated in FIG. 52.

[0174] When the thickness of the barrier film contiguous to the surface of the first-level interconnect M1 is smaller than that on the bottom of the contact hole, the geometrically shortest route of an electric current coincides with a thin portion of the barrier film PM2 a whose electric resistance becomes the lowest, which causes concentration of electrons (e), and deteriorates electromigration properties.

[0175] In this Embodiment, on the other hand, the film thickness E of the barrier film contiguous to the surface F of the first-level interconnect M1 is set greater than the film thickness B, the above-described effect is available.

[0176] In similar manners to those employed for the formation of the second-level interconnect M2 and connector portion (plug) P2, third-level to fifth-level interconnects M3 to M5 and connector portions (plugs) P1 to P5 are then formed. Illustrations and detailed description of them are however omitted.

[0177] In this Embodiment, the second-level interconnect M2 and connector portion (plug) 2 were formed using the dual damascene method. Alternatively, the second-level interconnect M2 and connector portion (plug) 2 were formed by separate steps by using the single damascene method as described in Embodiment 2. Also in this case, the above-described effect is available by setting the film thickness E of the barrier film PM2 a in the connector portion (plug) greater than the film thickness B.

[0178] The present invention made by the present inventors were described specifically based on Embodiments. The present invention is not limited by these Embodiments but can be modified within an extent not departing from the gist of the invention.

[0179] For examples, MISFETQn and Qp were given as examples of a semiconductor element. Not only MISFET but also another element such as bipolar transistor can be formed.

[0180] Effects available by the typical inventions, among the inventions disclosed by the present application, will next be described briefly.

[0181] (1) A conductive film on the bottom and sidewalls of a hole made in an insulating film formed over a semiconductor substrate is formed to increase its thickness from the center of the hole toward the side walls so that the geometrically shortest route of an electric current in the hole does not coincide with a thin portion of the conductive film at which electric resistance becomes the lowest, which makes it possible to disperse the route of electric current.

[0182] By such a constitution, concentration of electrons does not occur readily and electromigration properties can be improved. Moreover, the characteristics of a semiconductor integrated circuit device having such a conductive film can be improved.

[0183] As a result, an yield of the product can be heightened and its life (electromigration life) can be prolonged.

[0184] (2) When the bottom of the hole exists at a position deeper than the surface of the interconnect extending therebelow, a conductive film on the bottom and sidewalls is formed so that the film thickness E of the conductive film contiguous to the surface of the interconnect becomes greater than the film thickness B. The geometrically shortest route of an electric current in the hole therefore does not coincide with a thin portion of the conductive film at which electric resistance becomes the lowest, which makes it possible to disperse the route of electric current.

[0185] By such a constitution, concentration of electrons does not occur readily and electromigration properties can be improved. Moreover, the characteristics of a semiconductor integrated circuit device having such a conductive film can be improved.

[0186] As a result, an yield of the product can be heightened and its life (electromigration life) can be prolonged. 

What is claimed is:
 1. A semiconductor integrated circuit device, comprising: (a) an insulating film formed over a semiconductor substrate and having a hole; (b) a first conductive film formed on the bottom and sidewalls of said hole and increasing the thickness of the film from the center of the bottom toward the sidewalls of said hole; and (c) a second conductive film formed over said first conductive film and embedded inside of said hole.
 2. A semiconductor integrated circuit device according to claim 1, wherein said first conductive film increases the film thickness thereof from the center of the bottom toward the side walls of said hole all around a region defining the bottom of said hole.
 3. A semiconductor integrated circuit device according to claim 1, further comprising an interconnect exposed from the bottom of said hole, wherein said first conductive film increases the film thickness thereof from the center of the bottom toward the sidewalls of said hole at least in an extending direction of said interconnect.
 4. A semiconductor integrated circuit device, comprising: (a) an insulating film formed over a semiconductor substrate and having a hole; (b) a first conductive film formed on the bottom and sidewalls of said hole and having a declining portion declining from the sidewalls toward the center of the bottom of said hole; and (c) a second conductive film formed over said first conductive film and embedded inside of said hole.
 5. A semiconductor integrated circuit device according to claim 4, wherein said first conductive film has said declining portion declining from the sidewalls toward the center of the bottom of said hole all around a region defining the bottom of said hole.
 6. A semiconductor integrated circuit device according to claim 4, further comprising an interconnect exposed from the bottom of said hole, wherein said first conductive film has said declining portion declining from the sidewalls toward the center of the bottom of said hole at least in an extending direction of said interconnect.
 7. A semiconductor integrated circuit device, comprising: (a) an insulating film formed over a semiconductor substrate and having a hole; (b) a first conductive film formed on the bottom and sidewalls of said hole and being smaller in film thickness B at the center of the bottom of said hole than in film thickness A corresponding to a perpendicular line dropped toward the bottom of said hole from a shortest point from the corner of the bottom of said hole to the surface of said first conductive film; and (c) a second conductive film formed over said first conductive film and embedded inside of said hole.
 8. A semiconductor integrated circuit device according to claim 7, wherein said first conductive film formed on the bottom of said hole is smaller in said film thickness B than in said film thickness A all around a region defining the bottom of said hole.
 9. A semiconductor integrated circuit device according to claim 7, further comprising an interconnect exposed from the bottom of said hole, wherein said first conductive film is smaller in said film thickness B than in said film thickness A at least in an extending direction of said interconnect.
 10. A semiconductor integrated circuit device, comprising: (a) an insulating film formed over a semiconductor substrate and having a hole; (b) a first conductive film formed on the bottom and sidewalls of said hole and being lower in resistance at the center of the bottom of said hole than at a portion corresponding to a perpendicular line dropped toward the bottom of said hole from a shortest point from the corner of the bottom of said hole to the surface of said first conductive film; and (c) a second conductive film formed over said first conductive film and embedded inside of said hole.
 11. A semiconductor integrated circuit device according to claim 10, wherein said first conductive film is lower in resistance at the center of the bottom than at said portion all around a region defining the bottom of said hole.
 12. A semiconductor integrated circuit device according to claim 10, further comprising an interconnect exposed from the bottom of said hole, wherein said first conductive film is lower in resistance at the center than at said portion at least in an extending direction of said interconnect.
 13. A semiconductor integrated circuit device comprising: (a) a first interconnect formed over a semiconductor substrate; (b) a hole formed in an insulating film formed over said first interconnect and having a bottom from which the surface of said first interconnect is exposed; (c) a first conductive film formed on the bottom and sidewalls of said hole; (d) a second conductive film formed over said first conductive film and embedded inside of said hole; and (e) a second interconnect formed over said second conductive film, wherein a position at which the shortest pathway extending from said first interconnect toward said second interconnect through said first and second conductive films crosses over said first conductive film differs from a position at which said first conductive film has the lowest resistance.
 14. A semiconductor integrated circuit device comprising: (a) a first interconnect formed over a semiconductor substrate; (b) a hole formed in an insulating film formed over said first interconnect and having a bottom from which the surface of said first interconnect is exposed; (c) a first conductive film formed on the bottom and sidewalls of said hole; (d) a second conductive film formed over said first conductive film and embedded inside of said hole; and (e) a second interconnect formed over said second conductive film, wherein a position at which a shortest pathway extending from said first interconnect toward said second interconnect through said first and second conductive films crosses over said first conductive film does not coincide with a position at which said first conductive film has the lowest resistance.
 15. A semiconductor integrated circuit device, comprising: (a) an insulating film formed over a semiconductor substrate and having a hole; (b) a first conductive film formed on the bottom and sidewalls of said hole; (b₁) the film thickness B of said first conductive film at the center of the bottom of said hole being smaller than film thickness A corresponding to a perpendicular line dropped toward the bottom of said hole from the shortest point from the corner of the bottom of said hole to the surface of said first conductive film; (b₂) the film thickness B of said first conductive film at the center of the bottom of said hole being smaller than film thickness C corresponding to a perpendicular line dropped toward the sidewalls of said hole from a shortest point from the corner of the bottom of said hole to the surface of said first conductive film; and (c) a second conductive film formed over said first conductive film and embedded inside of said hole.
 16. A semiconductor integrated circuit device according to claim 15, wherein said first conductive film formed on the bottom of said hole is smaller in said film thickness B than said film thickness A and is smaller in said film thickness B than said film thickness C all around a region defining the bottom of said hole.
 17. A semiconductor integrated circuit device according to claim 15, further comprising an interconnect exposed from the bottom of said hole, wherein said first conductive film is smaller in said film thickness B than in said film thickness A and smaller in said film thickness B than in said film thickness C at least in an extending direction of said interconnect.
 18. A semiconductor integrated circuit device, comprising: (a) a first interconnect formed over a semiconductor substrate; (b) an insulating film formed over said first interconnect; (c) a hole formed in said first interconnect and said insulating film and having a bottom at a position deeper than the surface of said first interconnect; (d) a first conductive film which is formed on the bottom and sidewalls of said hole and, at the sidewalls of said hole, is greater in film thickness E at the sidewalls of said first conductive film contiguous to the surface of said first interconnect than in film thickness B at the center of the bottom of said hole; and (e) a second conductive film formed over said first conductive film and embedded inside of said hole.
 19. A semiconductor integrated circuit device, comprising: (a) a first interconnect formed over a semiconductor substrate; (b) an insulating film formed over said first interconnect; (c) a hole formed in said first interconnect and said insulating film and having a bottom at a position deeper than the surface of said first interconnect; (d) a first conductive film which is formed on the bottom and sidewalls of said hole, a portion of said first conductive film on the sidewalls contiguous to the surface of said first interconnect increasing the thickness of the film toward the bottom of the hole; and (e) a second conductive film formed over said first conductive film and embedded inside of said hole.
 20. A semiconductor integrated circuit device according to claim 19, wherein said first conductive film formed over the sidewalls of said hole increases the thickness of the film toward the bottom of said hole from a position above a portion contiguous to the surface of said first interconnect.
 21. A semiconductor integrated circuit device according to claim 1, wherein said first conductive film has a resistance greater than that of said second conductive film.
 22. A semiconductor integrated circuit device according to claim 1, wherein said first conductive film is a refractory metal film or a nitride thereof.
 23. A semiconductor integrated circuit device according to claim 1, wherein said first conductive film is made of tantalum (Ta), tantalum nitride (TaN), titanium (Ti), titanium nitride (TiN), tungsten (W), tungsten nitride (WN), titanium silicide nitride (TiSiN) or tungsten silicide nitride (WSiN), or an alloy thereof, or a laminate film thereof.
 24. A semiconductor integrated circuit device according to claim 1, wherein said second conductive film is a copper (Cu) film or an alloy thereof.
 25. A semiconductor integrated circuit device according to claim 1, wherein said first conductive film has at least the minimum film thickness permitting maintenance of barrier properties between said second conductive film and insulating film.
 26. A method of manufacturing a semiconductor integrated circuit device, comprising steps of: (a) forming a hole in an insulating film formed over a semiconductor substrate; (b) forming a first conductive film over the bottom and sidewalls of said hole; and (c) forming over said first conductive film a second conductive film and embedding therewith said hole, wherein said first conductive film is formed to increase the thickness thereof from the center of the bottom toward the sidewalls of said hole by ion bias sputtering.
 27. A method according to claim 26, wherein said first conductive film formed over the bottom of said hole increases the film thickness from the center of the bottom toward the sidewalls of said hole all round a region defining the bottom of said hole.
 28. A method of manufacturing a semiconductor integrated circuit device, comprising steps of: (a) forming a hole in an insulating film formed over a semiconductor substrate; (b) forming a first conductive film over the bottom and sidewalls of said hole; (c) forming over said first conductive film a second conductive film and embedding therewith inside of said hole, wherein said first conductive film is formed to have a declining portion declining from the sidewalls of said hole toward the center of the bottom by ion bias sputtering.
 29. A method according to claim 28, wherein said first conductive film formed over the bottom of said hole has a declining portion declining from the sidewalls of said hole toward the center of the bottom all around a region defining the bottom of said hole.
 30. A method according to claim 28, further comprising an interconnect exposed from the bottom of said hole, wherein said first conductive film has a declining portion declining from the sidewalls of said hole toward the center of the bottom at least in an extending direction of said interconnect.
 31. A method of manufacturing a semiconductor integrated circuit device, comprising steps of: (a) forming a hole in an insulating film formed over a semiconductor substrate; (b) forming a first conductive film over the bottom and sidewalls of said hole; (c) forming over said first conductive film a second conductive film and embedding therewith inside of said hole, wherein said first conductive film is formed to be smaller in film thickness B at the center of the bottom of said hole than in film thickness A corresponding to a perpendicular line dropped toward the bottom of said hole from a shortest point from the corner of the bottom of said hole to the surface of said first conductive film.
 32. A method according to claim 31, wherein said first conductive film formed over the bottom of said hole is smaller in said film thickness B than in said film thickness A all around a region defining the bottom of said hole.
 33. A method according to claim 31, wherein said semiconductor integrated circuit device has an interconnect exposed from the bottom of said hole, and wherein said first conductive film is smaller in said film thickness B than in said film thickness A at least in an extending direction of said interconnect.
 34. A method of manufacturing a semiconductor integrated circuit device, comprising steps of: (a) forming a hole in an insulating film formed over a semiconductor substrate; (b) forming a first conductive film over the bottom and sidewalls of said hole; (c) forming over said first conductive film a second conductive film and embedding therewith inside of said hole, wherein said first conductive film is formed by ion bias sputtering so that: (b₁) the film thickness B of said first conductive film at the center of the bottom of said hole is smaller than film thickness A corresponding to a perpendicular line dropped toward the bottom of said hole from the shortest point from the corner of the bottom of said hole to the surface of said first conductive film; and (b₂) the film thickness B of said first conductive film at the center of the bottom of said hole is smaller than film thickness C corresponding to a perpendicular line dropped toward the sidewalls of said hole from the shortest point from the corner of the bottom of said hole to the surface of said first conductive film.
 35. A method according to claim 34, wherein said first conductive film is smaller in said film thickness B than said film thickness A and is smaller in said film thickness B than said film thickness C all around a region defining the bottom of said hole.
 36. A method according to claim 34, wherein said semiconductor integrated circuit device has an interconnect exposed from the bottom of said hole, and wherein said first conductive film is smaller in said film thickness B than said film thickness A and smaller in said film thickness B than said film thickness C at least in an extending direction of said interconnect.
 37. A method of manufacturing a semiconductor integrated circuit device, comprising steps of: (a) forming a first interconnect over a semiconductor substrate; (b) forming an insulating film over said first interconnect; (c) forming, in said first interconnect and said insulating film, a hole having a bottom at a position deeper than the surface of said first interconnect; (d) forming a first conductive film over the bottom and sidewalls of said hole; and (e) forming over said first conductive film a second conductive film and embedding therewith inside of said hole, wherein said first conductive film is formed by ion bias sputtering to be greater in film thickness E at the sidewalls of said first conductive film contiguous to the surface of said first interconnect than in film thickness B at the center of the bottom of said hole.
 38. A method of manufacturing a semiconductor integrated circuit device, comprising: (a) forming a first interconnect over a semiconductor substrate; (b) forming an insulating film over said first interconnect; (c) forming, in said first interconnect and said insulating film, a hole having a bottom at a position deeper than the surface of said first interconnect; (d) forming a first conductive film over the bottom and sidewalls of said hole; and (e) forming over said first conductive film a second conductive film and embedding therewith inside of said hole, wherein said first conductive film is formed by ion bias sputtering so that the film thickness of a portion of said first conductive film formed over sidewalls contiguous to the surface of said first interconnect increases toward the bottom of the hole.
 39. A method according to claim 38, wherein said first conductive film formed over the sidewalls of said hole increases the film thickness toward the bottom of the hole from a position above a portion contiguous to the surface of said first interconnect.
 40. A method according to claim 26, wherein said first conductive film has film thickness more than the lowest thickness permitting maintenance of barrier properties between said second conductive film and insulating film and is a film of a refractory metal or a nitride thereof.
 41. A method according to claim 26, wherein said first conductive film is made of tantalum (Ta), tantalum nitride (TaN), titanium (Ti), titanium nitride (TiN), tungsten (W), tungsten nitride (WN), titanium silicide nitride (TiSiN) or tungsten silicide nitride (WSiN), or an alloy thereof, or a laminate film thereof.
 42. A method according to claim 26, wherein said second conductive film is a copper (Cu) film or a film of a copper alloy. 